NFA 53-707

COMPOSITION CHIMIQUE EN %
Cu | Sn | Pb | Zn | Fe | Ni |
---|---|---|---|---|---|
bal. | 6.0-8.0 | 5.0-7.0 | 2.0-5.0 | ≤ 0.20 | ≤ 1.5 |
Sb | S | P | Al | Mn | Si |
- | ≤ 0.10 | - | ≤ 0.01 | - | ≤ 0.01 |
CARACTERISTIQUES MECANIQUES
Erp0.2 N/mm2 | Rm N/mm2 | A% | H.B. | |
---|---|---|---|---|
Y70 | ≥ 120 | ≥ 260 | ≥ 12 | - |
Y80 | ≥ 120 | ≥ 260 | ≥ 12 | - |
NORMES EQUIVALENTES INTERNATIONALES (1)
- NFEN 1982 = CuSn7Zn4Pb7C – C/CC493K
- GAM-MM12 = CuSn7Pb6Zn4
- ISO 1338 = CuSn7Pb7Zn3
- DIN 1705 = CuSn7ZnPb (RG7)
- CDA (USA) = C93200 – ASTM B505 – B271
Indications d’emploi
- Frottement lubrifié.
- Charges moyennes.
- Vitesses moyennes.
- Pression 100/150 kg/cm2 maximum 250 kg/cm2.
- Température maximum d’utilisation 200°C.
- Douilles, raccords, coussinets, paliers, guides…
Bronze à l’étain CuSn7Pb6Zn4